A fluxing agent is commonly used to aid in wetting of the carbide to the steel. This may help mitigate some issues.
However, there are downsides.
The flux is corrosive and is difficult to evacuate, which results in voids under the tile (as shown in the images below) these voids are very common, and when located at an edge can allow the fluids in the centrifuge to enter and cause accelerated crevice corrosion and ultimately lead to the carbide disbonding from the backing plate.
Wear resistanceÌýof the carbide tile is always a concern, and JDBµç×Ó has that covered with our industry proven grades, but really the biggest issue we see in the market isÌýtile delamination.
Brazing preparation is a key concern.ÌýOils and other contaminants like surface oxidation on the carbide and steel components can prevent a good bond from forming. You can also have variability in the braze joint and quality of the bond depending on experience of the brazing technicians experience level.
Competitive Brazed TilesÌý-ÌýNote: White Areas are Voids
Our answer to these brazing challenges has been to apply our proven brazing technology and develop a total solution to eliminate the with decanter centrifuge tiles.ÌýResulting in a virtually void free bond between carbide and steel.
How do we achieve this?
- Multistep surface preparation with both carbide and steel
- Proprietary braze formula that is corrosion resistant andÌýdoes notÌýuse flux
- Our self-fixturing carbide mates to the steel for a consistent joint thickness and does not rely on the technician’s skill to achieve.
- Best in class, corrosion resistant carbide made from our own grades.
That is why we believe our tile is the most reliable tile offered to the rebuilder market today.
Ìý
JDBµç×Ó KDCT4 Brazed TilesÌý-ÌýVirtually Void Free
JDBµç×Ó’s Technical resources are second to none, it’s our not-so-secret weapon that has allowed us to develop the best centrifuge tile on the market. Our quality assurance and validation steps include:
- Ultrasonic C-Scan of braze joint
- Microstructure Evaluation of braze joint
- 100% visual inspection of external braze joint and of carbide
- ASTM G65 Procedure A – Abrasive Wear Testing
- Corrosion Testing – Gravimetric and Potentiostatic methods
- Salt Water Immersion Testing
- Rockwell Hardness Testing of Steel Backer after brazing
Explore JDBµç×Ó separation solutions.
Ìý
Related Articles
- Customer Case Study: Nozzle life improvement up to 25% with JDBµç×Ó ROCTEC APX!* Learn how one JDBµç×Ó customer saw nozzle life improvement up to 25% with ROCTEC APX Abrasive Waterjet Nozzles. Read now.Learn how one JDBµç×Ó customer saw nozzle life improvement up to 25% with ROCTEC APX Abrasive Waterjet Nozzles. Read now.
- Evaporator Boats and the Metallizing Process Evaporating metals to create a coating on your substrate is essential in the metallizing process. Learn about evaporator boats during the metallizing process.Evaporating metals to create a coating on your substrate is essential in the metallizing process. Learn about evaporator boats during the metallizing process.